SHT Multilayer Zirconia Block

Super-high-translucency zirconia block for CAD/CAM milling, available as SHT-C (white, A1-A3, B1-B2) and multilayer SHT-ML (A1-A3, B1-B2, BL1-4). Translucency is 49% and flexural strength is 900 MPa for both versions. Sintering is at 1500-1550 C (1530 C recommended) with a heating rate of up to 10 C/min and a 130-minute hold, then cooling in the closed furnace below 80 C.

Translucency

49%

Flexural strength

900 MPa

Sintering temperature

1500-1550 C (1530 C recommended)

Heating rate

up to 10 C/min

Hold time

130-minute